Z508 鎳銅鑄鐵焊條
標(biāo)準(zhǔn)：
符合GB EZNiCu-1
相當(dāng)AWS ENiCu-B
說明：
Z508是鎳銅合金（蒙乃爾）焊芯，強(qiáng)還原性石墨型藥皮的鑄鐵焊條。可交直流兩用，電弧穩(wěn)定，操作方便。焊縫金屬較軟但顏色比較亮，收縮率大，抗裂性比較差，焊縫強(qiáng)度也不高，故不宜用于受力部位和對新鑄件有色差要求的焊補(bǔ)。為了防止裂縫，對被焊母材推薦采用150~300℃低溫預(yù)熱，以減小焊接應(yīng)力。
Z508 is a nickel-copper alloy (Monel) core, cast iron electrode with strong reducing graphite coating. It can be used for both AC and DC, with stable arc and convenient operation. The weld metal is soft but the color is brighter, the shrinkage rate is large, the crack resistance is relatively poor, and the weld strength is not high, so it is not suitable for welding repairs on stressed parts and new castings with chromatic aberration requirements. In order to prevent cracks, it is recommended to use 150~300℃ low temperature preheating for the base material to be welded to reduce welding stress.
用途：
常用于強(qiáng)度要求不高的灰口鑄鐵氣孔及砂眼的補(bǔ)焊。
It is often used for repair welding of gray cast iron pores and blisters with low strength requirements.
熔敷金屬化學(xué)成分（%）
| C | Si | Mn | Ni | Cu | Fe | S |
| ≤1.0 | ≤0.80 | ≤2.50 | 60.0~70.0 | 25.0~35.0 | ≤6.0 | ≤0.025 |
參考電流：AC或DC
| 焊條直徑（mm） | 3.2 | 4.0 | 5.0 |
| 焊接電流（A） | 80~100 | 110~140 | 150~180 |
注意事項(xiàng)：
1. 首先清除焊接部位的油污、砂、水、銹等污物，并視缺陷類型，開坡口、打止裂孔及熔池造型等準(zhǔn)備措施。
2. 如填補(bǔ)大的空隙，應(yīng)先從四周開始堆焊一層，然后向中部逐步填滿。
3. 為避免母材熔化過多，減少白口層。施焊中，盡量采用小電流，短弧，窄道，短道，分散分段焊，每段焊道長度一般不超過50mm，待溫度降至不燙手時再繼續(xù)施焊。并且施焊后立即錘擊焊縫以松馳應(yīng)力防止裂紋。
4. 施焊前應(yīng)將焊條在150℃左右烘焙一小時。
1. First, remove oil, sand, water, rust and other contaminants from the welding part, and prepare measures such as beveling, cracking prevention, and molten pool modeling depending on the type of defect.
2. To fill a large gap, start from the surrounding area by surfacing one layer, and then gradually fill it up to the middle.
3. In order to avoid excessive melting of the base material, reduce the white mouth layer. In welding, try to use small current, short arc, narrow track, short track, dispersed segment welding, the length of each segment of the weld generally does not exceed 50mm, and continue welding when the temperature drops to not hot. And immediately after welding, hammer the weld to relax the stress and prevent cracks.
4. The welding rod should be baked at about 150℃ for one hour before welding.
相關(guān)產(chǎn)品
白銅焊條Cu307
Z308 純鎳鑄鐵焊條
焊補(bǔ)鑄鐵用的鎳基鑄鐵焊條在鑄鐵焊接中屬于異質(zhì)焊縫的冷態(tài)焊焊條。藥皮為強(qiáng)還原性石墨型，交直流兩用，工藝性能良好，可全位置焊接。焊縫金屬不存在硬而脆的CFe3（滲碳體）即白口組織，所以焊縫金屬具有良好的加工性和承受塑性變形的能力。但熔合區(qū)由于母材成分熔化的影響，仍不可避免地會有不同程度的白口組織。為了減輕熔合區(qū)硬脆組織對焊后加工性能的不良影響，使其白口層盡量較少，較薄、且不連續(xù)，施焊時應(yīng)該嚴(yán)格遵循冷焊工藝規(guī)定操作。另外，某些鑄件（如長期在高溫、水蒸氣中工作的爐柵，鍋爐等），因其中的碳已被燒損，鑄件具有多空性，變得十分松脆而無法焊、補(bǔ)。
Z408 鎳鐵鑄鐵焊條
焊補(bǔ)鑄鐵用的鎳基鑄鐵焊條在鑄鐵焊接中屬于異質(zhì)焊縫的冷態(tài)焊焊條。藥皮為強(qiáng)還原性石墨型，交直流兩用，工藝性能良好，可全位置焊接。焊縫金屬不存在硬而脆的CFe3（滲碳體）即白口組織，所以焊縫金屬具有良好的加工性和承受塑性變形的能力。但熔合區(qū)由于母材成分熔化的影響，仍不可避免地會有不同程度的白口組織。為了減輕熔合區(qū)硬脆組織對焊后加工性能的不良影響，使其白口層盡量較少，較薄、且不連續(xù)，施焊時應(yīng)該嚴(yán)格遵循冷焊工藝規(guī)定操作。另外，某些鑄件（如長期在高溫、水蒸氣中工作的爐柵，鍋爐等），因其中的碳已被燒損，鑄件具有多空性，變得十分松脆而無法焊、補(bǔ)。
Z508 鎳銅鑄鐵焊條
焊補(bǔ)鑄鐵用的鎳基鑄鐵焊條在鑄鐵焊接中屬于異質(zhì)焊縫的冷態(tài)焊焊條。藥皮為強(qiáng)還原性石墨型，交直流兩用，工藝性能良好，可全位置焊接。焊縫金屬不存在硬而脆的CFe3（滲碳體）即白口組織，所以焊縫金屬具有良好的加工性和承受塑性變形的能力。但熔合區(qū)由于母材成分熔化的影響，仍不可避免地會有不同程度的白口組織。為了減輕熔合區(qū)硬脆組織對焊后加工性能的不良影響，使其白口層盡量較少，較薄、且不連續(xù)，施焊時應(yīng)該嚴(yán)格遵循冷焊工藝規(guī)定操作。另外，某些鑄件（如長期在高溫、水蒸氣中工作的爐柵，鍋爐等），因其中的碳已被燒損，鑄件具有多空性，變得十分松脆而無法焊、補(bǔ)。
Cu107 紫銅焊條
銅及銅合金焊條用途較廣，除了用紫銅焊條焊接紫銅外，目前采用較多的是用青銅焊條來焊接銅及銅合金、銅與鋼等。但銅及其合金的弧焊一般較鋼困難。這是由于銅及銅合金焊接時易產(chǎn)生金屬氧化、元素?zé)龘p、以及氣孔、裂縫和變形等。另外，銅及其合金的導(dǎo)熱性特別高致使焊條在引弧后往往不能使母材熔融，而產(chǎn)生熔滴飛散，故焊接銅及銅合金時該類焊件焊前必須要有合理的預(yù)熱及用較大的焊接電流、直流反接，短弧垂直。焊后應(yīng)對焊縫進(jìn)行適當(dāng)錘擊，以消除應(yīng)力及細(xì)化晶粒。另外，銅及其合金塑性好且不溶解碳，也不與碳化合生成脆硬組織，故銅及銅合金焊條也能用來焊補(bǔ)鑄鐵。