S201 紫銅氬弧焊絲
銅及銅合金焊絲常用于焊接銅及銅合金，其中黃銅焊絲也廣泛用于釬焊碳鋼、鑄鐵及硬質(zhì)合金刀具等。選用適當(dāng)?shù)暮附z進(jìn)行氬弧焊是保證銅及青銅焊接質(zhì)量的有效方法之一，不但可獲得性能良好的焊縫而且有利于減少焊件變形。用氧-乙炔氣焊時(shí)應(yīng)配合銅氣焊熔劑使用,或使用已包有銅氣焊熔劑的銅焊絲。碳弧焊也是焊接銅及銅合金的常用方法之一，碳弧焊的焊接工藝和氣焊類似，焊絲及熔劑也和氣焊時(shí)一樣。
所屬分類： 銅及銅合金焊絲
產(chǎn)品詳情
標(biāo)準(zhǔn)：
GB SCu1898
相當(dāng)AWS ERCu
說明：
S201是含有少量硅、錳、磷等脫氧元素的特制紫銅焊絲。加入錫改善了熔融銅的流動(dòng)性。具有焊接工藝性能優(yōu)良、焊縫成型良好、機(jī)械性能高、抗裂性好等優(yōu)點(diǎn)。
S201 is a special red copper welding wire containing a small amount of deoxidizing elements such as silicon, manganese, and phosphorus. The addition of tin improves the fluidity of molten copper. It has the advantages of excellent welding process performance, good weld formation, high mechanical properties, and good crack resistance.
用途：
用于紫銅氬弧焊及氧-乙炔氣焊時(shí)作為填充材料。
Used as a filling material for argon arc welding of red copper and oxygen-acetylene gas welding.
焊絲化學(xué)成分：
| Mn | Si | Sn | P | Cu |
| 0.2~0.5 | 0.2~0.5 | 0.5~1.0 | 0.02~0.15 | 余量 |
供應(yīng)規(guī)格（mm）：
| 盤裝Φ | 0.6 | 0.8 | 0.9 | 1.0 | 1.2 | 10.5 | |
| 焊絲直徑Φ （長(zhǎng)度1000） |
1.5 | 2.0 | 2.5 | 3.0 | 4.0 | 5.0 | 6.0 |
注意事項(xiàng)：
1. 工件焊接邊緣和焊絲表面的氧化物、油等污物在焊接前必須清除干凈，否則會(huì)引起氣孔、夾渣等缺陷，使焊縫性能降低。
2. 對(duì)接接頭板厚小于3mm時(shí)，不開坡口；板厚為3~10mm時(shí)，開60°~70°V型坡口；板厚大于10mm時(shí)，開60°~70°X型坡口。為避免未焊透，一般不留鈍邊。
3. 焊前工件必須預(yù)熱。板厚小于3mm預(yù)熱溫度為150~300℃；板厚大于3mm時(shí)，預(yù)熱溫度為350~500℃。
4. 進(jìn)行TIG焊時(shí)用直流正極性焊接，以獲得最大的熔透深度。
1. The oxides, oil and other dirt on the welding edge of the workpiece and the surface of the welding wire must be removed before welding, otherwise it will cause defects such as pores and slag inclusions and reduce the performance of the weld.
2. When the plate thickness of the butt joint is less than 3mm, no groove; when the plate thickness is 3~10mm, 60°~70°V groove; when the plate thickness is greater than 10mm, 60°~70°X groove . In order to avoid incomplete welding, generally no blunt edges are left.
3. The workpiece must be preheated before welding. The preheating temperature for plate thickness is less than 3mm is 150~300℃; when the plate thickness is greater than 3mm, the preheating temperature is 350~500℃.
4. When performing TIG welding, use DC positive polarity welding to obtain the maximum penetration depth.
合作意向表
如您有任何形式的合作意向，歡迎在此留下您的信息，我們將很快與您聯(lián)絡(luò)。
銅及銅合金焊絲常用于焊接銅及銅合金，其中黃銅焊絲也廣泛用于釬焊碳鋼、鑄鐵及硬質(zhì)合金刀具等。選用適當(dāng)?shù)暮附z進(jìn)行氬弧焊是保證銅及青銅焊接質(zhì)量的有效方法之一，不但可獲得性能良好的焊縫而且有利于減少焊件變形。用氧-乙炔氣焊時(shí)應(yīng)配合銅氣焊熔劑使用,或使用已包有銅氣焊熔劑的銅焊絲。碳弧焊也是焊接銅及銅合金的常用方法之一，碳弧焊的焊接工藝和氣焊類似，焊絲及熔劑也和氣焊時(shí)一樣。
銅及銅合金焊絲常用于焊接銅及銅合金，其中黃銅焊絲也廣泛用于釬焊碳鋼、鑄鐵及硬質(zhì)合金刀具等。選用適當(dāng)?shù)暮附z進(jìn)行氬弧焊是保證銅及青銅焊接質(zhì)量的有效方法之一，不但可獲得性能良好的焊縫而且有利于減少焊件變形。用氧-乙炔氣焊時(shí)應(yīng)配合銅氣焊熔劑使用,或使用已包有銅氣焊熔劑的銅焊絲。碳弧焊也是焊接銅及銅合金的常用方法之一，碳弧焊的焊接工藝和氣焊類似，焊絲及熔劑也和氣焊時(shí)一樣。
銅及銅合金焊絲常用于焊接銅及銅合金，其中黃銅焊絲也廣泛用于釬焊碳鋼、鑄鐵及硬質(zhì)合金刀具等。選用適當(dāng)?shù)暮附z進(jìn)行氬弧焊是保證銅及青銅焊接質(zhì)量的有效方法之一，不但可獲得性能良好的焊縫而且有利于減少焊件變形。用氧-乙炔氣焊時(shí)應(yīng)配合銅氣焊熔劑使用,或使用已包有銅氣焊熔劑的銅焊絲。碳弧焊也是焊接銅及銅合金的常用方法之一，碳弧焊的焊接工藝和氣焊類似，焊絲及熔劑也和氣焊時(shí)一樣。
丹陽申澳焊接材料有限公司
電話：133 7604 8635 0511-867380801
傳真：0511-86738080
地址：江蘇省鎮(zhèn)江丹陽市訪仙鎮(zhèn)工業(yè)區(qū)
微信客服